Mechanical properties: Tensile strength σb (MPa): ≥430 Conditions yield strength σ0.2 (MPa): ≥275 Elongation δ5 (%): ≥10 Note: The

Features and Scope: Alloy rivets. With high shear strength and heat resistance, pressure processing performance and cutting performance and corrosion resistanc

2A06 aluminum alloy for high strength aluminum hard, pressure processing performance and cutting and 2A12 same, just in the annealed and quenched state plastic

Quenching and aging: hardening 530 ~ 540 ℃, water cooling; artificial aging (forgings, sheet) 160 ~ 170 ℃, 10 ~ 16h, air-cooled; natural aging at room temperature Anytime.

● Mechanical Properties Tensile strength σb (MPA): ≥315 Elongation δ5 (%): ≥4 Note: The vertical bar at room temperature mechanical properti

2A11 aluminum is the first application of a hard aluminum, commonly referred to as a standard hard aluminum.

2A10 aluminum alloys are the rivets. High shear strength, annealing, just quenching, aging and thermal state have sufficient plasticity rivet is required; with riveted after quenching and aging, the time limit is not heat-treated after the riveting proces

Alloy rivets. 2A02 shear strength and considerable, other properties and 2B11 similar, but rivets must be riveted within 20min after quenching, it is difficult to process, and thus the application range is limited

2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance. Many countries are producing

Belong to Al-Zn-Mg-Cu based hard aluminum alloy rivets. Quenching artificial aging state can be riveting, a high-strength rivets material when the temperature is below 100 ℃.

7A09 aluminum mechanical properties: Tensile strength σb (MPa): ≥530 Tensile stress σp0.2 (MPa): ≥400

In HYLR5000 or KYNAR500 as the base material PVDF coating corrosion, pollution, weathering has unique advantages, both in the hot sun or cold wind and snow are destructive beautiful appearance.

2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance.

Insulation is a high-grade aluminum exterior decoration materials in construction has a lot of use, because of its outstanding features were broad features the company's trust.

6063 Mg-Si alloy is formulated as the main alloying element, the content of each element has a certain range, the high price of magnesium.

Medium strength, corrosion resistance, good welding performance, process performance (easy to squeeze out of shape) good coloring properties.

Aluminum alloy 7005 is stronger than 7003. Due to aluminum alloy 7005 have good weld ability, it often use for structural parts.

Aluminum wheels price is about 2 to 3 times the drum, the benefits of its use is much higher than the drum:

High-quality 8000 series aluminum rod should be high-strength, high conductivity, silk bright, stable properties.

6082 belongs to 6 ××× series (Al-Mg-Si) aluminum alloy, is able to heat treatment of aluminum alloy sheet strengthened, with moderate strength and good weld ability, corrosion resistance, mainly for transport and structural engineering industry.

Also known as work hardening process to strengthen that metallic material below the recrystallization temperature of cold deformation processing, such as forging, rolling, drawing, stretching, cold deformation, the metal inside the dislocation density inc

Foil stamping is a direct material rolled into sheet metal aluminum, which is similar to its effect with pure silver stamping effect, so called fake silver.

First, the rolling processAluminum surface degreasing and chemical treatment, roll quality paint, dry cured from. Flatness of the surface of the film rolls pla

Depending on the metal elements containing aluminum, aluminum can be divided into nine categories, that is, aluminum can be divided into nine series:

. Aluminum printing machine can also print pattern text on any material. Such as: ceramics, gold, silver iron aluminum, crystal materials, wood, glass, leather, cloth, stone, ABS, PVC