  • Apr 22,2015

    Quenching and aging: hardening 530 ~ 540 ℃, water cooling; artificial aging (forgings, sheet) 160 ~ 170 ℃, 10 ~ 16h, air-cooled; natural aging at room temperature Anytime.

  • Apr 21,2015

    ● Mechanical Properties Tensile strength σb (MPA): ≥315 Elongation δ5 (%): ≥4 Note: The vertical bar at room temperature mechanical properti

  • Apr 21,2015

    2A11 aluminum is the first application of a hard aluminum, commonly referred to as a standard hard aluminum.

  • Apr 20,2015

    2A10 aluminum alloys are the rivets. High shear strength, annealing, just quenching, aging and thermal state have sufficient plasticity rivet is required; with riveted after quenching and aging, the time limit is not heat-treated after the riveting proces

  • Apr 20,2015

    Alloy rivets. 2A02 shear strength and considerable, other properties and 2B11 similar, but rivets must be riveted within 20min after quenching, it is difficult to process, and thus the application range is limited

  • Apr 20,2015

    2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance. Many countries are producing

  • Apr 20,2015

    Belong to Al-Zn-Mg-Cu based hard aluminum alloy rivets. Quenching artificial aging state can be riveting, a high-strength rivets material when the temperature is below 100 ℃.

  • Apr 16,2015

    7A09 aluminum mechanical properties: Tensile strength σb (MPa): ≥530 Tensile stress σp0.2 (MPa): ≥400

  • Apr 16,2015

    In HYLR5000 or KYNAR500 as the base material PVDF coating corrosion, pollution, weathering has unique advantages, both in the hot sun or cold wind and snow are destructive beautiful appearance.

  • Apr 15,2015

    2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance.