2A11 aluminum is the first application of a hard aluminum, commonly referred to as a standard hard aluminum.

2A10 aluminum alloys are the rivets. High shear strength, annealing, just quenching, aging and thermal state have sufficient plasticity rivet is required; with riveted after quenching and aging, the time limit is not heat-treated after the riveting proces

Alloy rivets. 2A02 shear strength and considerable, other properties and 2B11 similar, but rivets must be riveted within 20min after quenching, it is difficult to process, and thus the application range is limited

2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance. Many countries are producing

Belong to Al-Zn-Mg-Cu based hard aluminum alloy rivets. Quenching artificial aging state can be riveting, a high-strength rivets material when the temperature is below 100 ℃.

7A09 aluminum mechanical properties: Tensile strength σb (MPa): ≥530 Tensile stress σp0.2 (MPa): ≥400

In HYLR5000 or KYNAR500 as the base material PVDF coating corrosion, pollution, weathering has unique advantages, both in the hot sun or cold wind and snow are destructive beautiful appearance.

2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance.

Insulation is a high-grade aluminum exterior decoration materials in construction has a lot of use, because of its outstanding features were broad features the company's trust.

6063 Mg-Si alloy is formulated as the main alloying element, the content of each element has a certain range, the high price of magnesium.