7A03 Aluminum Performance

2015-05-04

Features and Scope:

 

It belongs to Al-Zn-Mg-Cu based hard aluminum alloy rivets. Quenching artificial aging state can be riveting, high-strength rivets material temperature is below 100 , the. Heat treatment can be enhanced, high shear strength, corrosion resistance and machinability is still good, quenching using artificial aging state; rivet rivets, without restrictions after the heat treatment time; the general corrosion resistance is acceptable, there is stress corrosion cracking tendencies.

 

Mechanical Properties:

 

Shear strength τ (MPa): 284

 

NOTE: After the wire solution heat treatment to natural aging stable-state shear

 

Sample size: All wire diameter

 

Heat Specifications:

 

1) Complete annealing: heating 390 ~ 430 ; with the effective thickness of different materials, holding time between the 30 ~ 120min; with / h speed of 30 ~ 50 , with furnace cooling to below 150 , and then air cooled.

 

2) Quenching and aging: hardening 460 ~ 470 , water-cooled; artificial

 

( Aging stage aging) Level 1 115 ~ 125 3 ~ 4h heating, Level 2 160 ~ 170 , 3 ~ 5h, cooled.

 

Status: Rivet aluminum and aluminum alloy wire (T6 state)